Polycarboxylate superplasticizer PCEse konpoze de konpoze macromolekilè ak gwoup asid sulfonic, gwoup karboksil, gwoup amine, ak chenn bò polyoxyethylene, elatriye, nan solisyon akeuz, nan prensip la nan sentèz lib radikal copolymerization nan polymère ak yon estrikti estrikti peny.

Materyèl yo anvan tout koreksyon prensipal ki nesesè pou sentèz la nanKonstriksyon chimik dlo redukteur polycarboxylate superplasticierare: methacrylic acid, acrylic acid, ethyl acrylate, hydroxyethyl acrylate, sodium allyl sulfonate, methyl methacrylate, 2-acrylamido- 2-Methacrylic acid, methoxy polyoxyethylene methacrylate, ethoxy polyethylene glycol acrylate, allyl ether, etc. Inisyasyon yo ki ka itilize nan pwosesis la polimerizasyon yo se: persulfate ki baze sou amorseur, oksijene benzoyl, azobisisobutyl cyanide; Ajan transfè chèn: 3-mercaptopropionic asid, asid mercaptoacetic, elatriye.

Asid polycarboxylic dlo a diminye ajan Metòd sentèz se: nan yon flakon anba wonn ekipe ak yon ajitasyon elektrik, yon tèmomèt, yon aparèy jete, ak yon kondansateur rflu, solisyon an monomè polimerizasyon ak solisyon an amors yo tou dousman te ajoute dropwise pa metòd la nan chofaj nan yon beny dlo. Lè w ap chwazi monomè polimerizasyon an, inivèsite a ak to konpetisyon li yo ta dwe konplètman konsidere kòm. Tanperati reyaksyon an ka detèmine dapre kalite reyaksyon espesifik monomè. Anjeneral, yo ka chwazi tanperati a nan ranje tanperati a nan 70 ~ 95 ℃ kòm tanperati reyaksyon an.

Drop solisyon an monomè nan yon sèl moman, ak Lè sa a, lage l 'nan 20 minit ajoute solisyon an ki rete inisyasyon, epi finalman ogmante tanperati a pa 5 ° C, kontinye reyaksyon an pou 1H, epi apre tanperati a bese a 40 ° C, netralize ak egzeyat.